1 Scope
This part of GB/T 3098 specifies mechanical and physical properties of bolts, screws and studs made of carbon steel or alloy steel when tested at an ambient environment temperature range of 10℃ to 35℃. Within the range of this environment temperature, as for fasteners (including bolts, screws and studs, the same below) that conform to the technical requirements of this part, at higher (See Appendix 8) and/or lower temperature, they are possible to fail to conform to the specified mechanical and physical properties.
Note: 1 Fasteners conforming to the requirements of this part are used in applications from -50℃~ to 150℃. Users are advised to consult with the parties concerned for temperatures outside the range of -50℃~ to 150℃ and up to a maximum temperature of +300℃.
2 Information for the selection and application of low temperature and high temperature steels is given, for example, in EN 10269[1], ASTM F2281[3] and ASTM A320/A320M[4].
Certain fasteners might not fulfill the tensile or torsion requirements of this part because the geometry of their heads reduces the shear area in the head. These include fasteners having a low head, with or without external driving feature, a low round or cylindrical head with internal driving feature or a countersunk head with internal driving feature (see Section 8.2).
This part is applicable to fasteners:
a) Made of carbon steel or alloy steel;
b) Common threads that meet those specified in GB/T 192;
c) With coarse thread 1.6 to M39 and fine pitch thread M8*1 to M39*3;
d) With diameter/pitch combinations according to GB/T 193;
e) Having tolerances according to GB/T 197, GB/T 9145 and GB/T 22029;
This part is not applicable to set screws and similar threaded fasteners not under tensile stresses (see GB/T 3098.3).
This part doesn't not specify requirements for such properties as:
- Weldability;
- Corrosion resistance;
- Resistance to shear stress;
- Torsion/clamp force performance; or
- Fatigue resistance.
2 Normative References
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
GB/T 90.3 Fasteners - Quality Assurance System (GB/T 90. 3-2010, ISO 16426: 2002, IDT)
GB/T 192 General Purpose Metric Screw Threads - Basic Profile (ISO 68-1: 1998, IS0 General Purpose Screw Threads - Basic Profile - Part 1: Metric Screw Threads, MOD);
GB/T 193 General Purpose Metric Screw Threads - General Plan (ISO 261: 1998, ISO General Purpose Metric Screw Threads - General Plan, MOD);
GB/T 196 General Purpose Metric Screw Threads - Basic dimensions (ISO 724: 1993, ISO General Purpose Metric Screw Threads - Basic Dimensions, MOD);
GB/T 197 Gneral Purpose Metric Screw Threads - Tolerances (ISO 965-1: 1998, ISO General Purpose Metric Screw Threads - Tolerances - Part 1: Principles and Basic Data, MOD);
GB/T 228.1 Metallic Materials - Tensile Testing - Part 1: Method of Test at Room Temperature (GB/T 228.1-2010, ISO 6892-1: 2009, MOD);
GB/T 229 Metallic Materials - Charpy Pendulum Impact Test Method (GB/T 229-2007, ISO 148-1: 2006, MOD);
GB/T 230.1 Metallic Materials - Rockwell Hardness Test - Part 1: Test method (Scales A, B, C, D, E, F, G, H, K, N and T) (GB/T 230.1-2009, ISO 6508-1: 2005, MOD);
GB/T 231.1 Metallic Materials - Brinell Hardness Test - Part 1: Test Method;
GB/T 3098.2 Mechanical Properties of Fasteners - Nuts - Coarse Thread (GB/T 3098.2-2000, idt ISO 898-2: 1992);
GB/T 3098.3 Mechanical Properties of Fasteners - Set Screw (GB/T 3098.3-2000, idt ISO 898-5: 1998);
GB/T 3098.13 Mechanical Properties of Fasteners - Torsional Test and Minimum Torques for Bolts and Screws with Nominal Diameters 1mm to 10mm (GB/T 3098.13-1996, idt ISO 898-7: 1992);
GB/T 4340.1 Metallic Materials - Vickers Hardness Test - Part 1: Test Method (GB/T 4340.1-2009, ISO 6507-1: 2005, MOD);
GB/T 5267.1 Fasteners - Electroplated Coatings (GB/T 5267.1-2002, ISO 4042: 1999, IDT)
GB/T 5267.2 Fasteners - Non-electrolytically Applied Zinc Flake Coatings (GB/T 5267.2-2002, ISO 10683: 2000, IDT);
GB/T 5267.3 Fasteners - Hot Dip Galvanized Coatings (GB/T 5267.3-2008, ISO 10684: 2004, IDT);
GB/T 5267 Fasteners - Bolts, Screws, Studs and Nuts - Symbols and Designations of Dimensions (GB/T 5276-1985, eqv ISO 225: 1983);
GB/T 5277 Fasteners - Clearance Holes for Bolts and Screws (GB/T 5277-1985, eqv ISO 273: 1979);
GB/T 5779.1 Fasteners - Surface Discontinuities - Bolts, Screws and Studs for General Requirements (GB/T 5779.1-2000, idt ISO 6157-1: 1988);
GB/T 5779.3 Fasteners - Surface Discontinuities - Bolts, Screws and Studs for Special Requirements (GB/T 5779.3-2000, idt ISO 6157-3: 1988);
GB/T 9144 Gneral Purpose Metric Screw Threads - Preferable Plan (GB/T 9144-2003, ISO 262: 1998, ISO Gneral Purpose Metric Screw Threads - Selected Sizes for Screws, Bolts and Nuts, MOD);
GB/T 9145 Gneral Purpose Metric Screw Threads - Limit of Sizes for the Screw Threads of Medium Quality and Preferable Plan (GB/T 9145-2003, ISO 965-2: 1998, ISO General Purpose Metric Screw Threads - Tolerances - Limit of Sizes for General Purpose External and Internal Screw Threads - Medium Quality, MOD);
GB/T l6825.1-2002 Verification of Static Uniaxial Testing Machines - Part 1: Tension and (or) compression Testing Machines - Verification and Calibration of the Force - Measuring System (idt ISO 7500-1: 2004, IDT);
GB/T 22029 Hot-dip Galvanized Screw Threads - On External Screw Threads There is the Clearance for Accommodating the Hot-dip Galvanized Coat (GB/T 22029-2008, ISO 965-4: 1998, ISO General Purpose Metric Screw Threads - Tolerances - Part 4: Limit of Sizes for Hot-dip Galvanized External Screw Threads to Mate with Internal Screw Threads Tapped with Tolerance Position H or G after Galvanizing, MOD);
ISO 4885: 1996 Ferrous Products - Heat Treatment – Vocabulary.
3 Terms and Definitions
For the purpose of this part, the following terms and definitions apply.
3.1
Finished fastener
Fastener for which all manufacturing steps have been completed, with or without any surface coating and with full or reduced loadability, and which has not been machined into a test piece.
3.2
Machined test piece
Test pieces machined from a fastener to evaluate material properties.
3.3
Full-size fastener
Finished fastener with a shank diameter of ds≈d or ds>d, or or fully threaded screws (bolts) or studs (screw shank).
3.4
Fastener with waisted shank
Finished fastener with the shank diameter ds
1 Scope
2 Normative References
3 Terms and Definitions
4 Symbols and Abbreviated Terms
5 Designation System for Property Classes
6 Materials
7 Mechanical and Physical Properties
8 Applicability of Test Methods
9 Test Methods
10 Marking
10 Marking
Appendix A (Informative) Relation Between Tensile Strength And Elongation After Fracture
Appendix B (Informative) Influence of Elevated Temperatures on Mechanical Properties of Fasteners
Appendix C (Informative) Elongation After Fracture for Full-Size Fasteners, Αf
Bibliography