标准编号:	GB/T 22374-2018
中文名称:	地坪涂装材料
英文名称:	Floor coating
中标分类:	Q18    装修材料
行业分类:	GB    国家标准
发布机构:	国家市场监督管理总局 国家标准化管理委员会
发布日期:	2018-06-07
实施日期:	2019-5-1
标准状态:	valid
替代旧标准:	GB/T 22374-2008 地坪涂装材料
翻译语言:	英文
文件格式:	PDF
中文字符数:	25000 字
翻译价格(元):	1750.0
交付时间:	付款后 1 个工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed in accordance with the rules given in GB/T 1.1-2009. This standard replaces GB/T 22374-2008 Floor coatings. In addition to a number of editorial changes, the following technical changes have been made with respect to GB/T 22374-2008 (the previous edition): ——the terms and definitions are modified (see Clause 3; Clause 3 in Edition 2008); ——the product classification is modified (see 4.1; 4.1 in Edition 2008); ——the items “total content of glycol ether and ether ester, total content of phthalic acid esters, free 4,4'-diaminodiphenylmethane (MDA), total volatile organic compound (TVOC) emission and formaldehyde emission" are added (see Table 1; Table 2 in Edition 2008); ——the item "stretching adhesive strength" is added in and “adhesion” is deleted from priming coat (see Table 2; Table 3 in Edition 2008); ——the technical requirements for floating coat of floor coatings are added (see Table 3); ——in top coat basic performance “stretching adhesive strength” is added for waterborne and solvent-borne floor coatings, “artificial weather resistance” for outdoor floor coating, “initial fluidity” for self-leveling floor coating, and “adhesion” is deleted from it (see Table 4; Table 4 in Edition 2008); ——the technical requirements for top coating of polymer cement floor coating are added (see Table 5); ——in top coat special performance items “elasticity”, “coating resistance to temperature change”, “scratch resistance” and “hot tire indentation resistance” are added, and “fluidity”, “stretching adhesive strength” and “artificial weather resistance” are deleted (see Table 6; Table 5 in Edition 2008); ——the test methods for volatile organic compound (VOC) content and free formaldehyde are modified (see 6.2.3, 6.2.4; 6.3.1 and 6.3.2 in Edition 2008); ——the test substrate is changed from asbestos cement sheet into non-asbestos fiber cement flat sheet (see 6.3.1.1.1; 6.2.1.1 in Edition 2008). ——the normative Annex B is added (see Annex B) and the normative Annex A is modified (see Annex A; Annex A in Edition 2008). This standard was proposed by China Building Materials Federation. This standard is under the jurisdiction of SAC/TC 195 National Technical Committee on Constructional Materials and Decorative Materials of Standardization Administration of China. The previous edition of standard replaced by this standard is as follows: ——GB/T 22374-2008. Floor coatings 1 Scope This standard specifies terms and definitions, classification and mark, requirements, test methods, inspection rules, marking, packaging, transport and storage of floor coatings. This standard is applicable to synthetic resin-based and polymer cement floor coating applied to cement mortar, concrete and other base surfaces for decoration, protection and special functions like anti-static, anti-slip, etc. of the ground. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 250 Textiles - Tests for color fastness - Grey scale for assessing change in color GB/T 1633-2000 Plastics - Thermoplastic materials - Determination of vicat sofening temperature (VST) GB/T 1728-1979 Methods of test for drying time of coatings of paints and putties GB/T 1731 Determination of flexibility of films GB/T 1766 Paints and varnishes - Rating schemes of degradation of coats GB/T 1768 Paints and varnishes - Determination of resistance to abrasion - Rotating abrasive rubber wheel method GB/T 1865-2009 Paints and varnishes - Artificial weathering and exposure to artificial radiation - Exposure to filtered xenon-arc radiation GB/T 2411-2008 Plastics and ebonite - determination of indentation hardness by means of a duronmeter (Shore Hardness) GB/T 2567-2008 Test methods for properties of resin casting body GB/T 4100-2015 Ceramic tile GB/T 6682 Water for analytical laboratory use - Specification and test methods GIVT 6739 Paints and varnishes - Determination of film hardness by pencil test GB/T 8170 Rules of rounding off for numerical values & expression and judgement of limiting values GB 8624 Classification for burning behavior of building materials and products GB/T 9271 Paints and varnishes - standard panels for testing GB/T 9274-1988 Paints and varnishes - Determination of resistance to liquids GB 9743 Passenger car tyres GB/T 9754 Paints and varnishes - Determination of specular gloss of non-metallic paint films at 20°, 60°and 85° GB/T 9779-2015 Multi-layer coatings for architecture GB/T 9780-2013 Test method for dirt pickup resistance and stain removal of film of architectural coatings and paint GB/T 11186.2-1989 Methods for measuring the colour of paint films - Part 2: Colour measurement GB 11614 Plate glass GB/T 13491 General rule for packing of coatings GB/T 17671 Method of testing cements - Determination of strength (ISO Method) GIVT 18446 Binders for paints and varnishes - determination of monomeric diisocyanates in isocyanate resins GB 18581-2009 Indoor decorating and refurbishing materials - Limit of harmful substances of solvent based coatings for woodenware GB 18582-2008 Indoor decorating and refurbishing materials - Limit of harmful substances of interior architectural coatings GB 18583-2008 Indoor decorating and refurbishing materials - Limit of harmful substances of adhesives GB/T 23985-2009 Paints and varnishes - Determination of volatile organic compound (VOC) content - Difference method GB/T 23993 Determination of formaldehyde content of waterborne coatings - Spectrophtometric method with acetylacetone GB 24408-2009 Limit of harmful substances of exterior wall coatings GB 24613 Limit of harmful substances of coatings for toys JC/T 412.1-2006 Fiber cement flat sheets - Part 1: Non-asbestos fiber cement flat sheets JC/T 547 Adhesives for ceramic tiles JC/T 985-2017 Cementitious self-leveling floor mortar JC/T 2327-2015 Waterborne polyurethane screed material JG/T 25 Test method for temperature change resistance of architectural coatings JG/T 481-2015 Water-based interior wall coating with low-emission volatile organic compounds (VOC) SJ/T 11294 General specification of floor coating for electrostatic protection YB/T 4086-2017 Steel wool fiber 3 Terms and definitions For the purpose of this document, the terms and definitions given in GB 18582-2008 and JG/T 481-2015 and the following apply. 3.1 volatile organic compound (VOC) all organic compounds of which the initial boiling point is lower than or equal to 250℃ under the standard atmosphere pressure 101.3kPa [GB 18582-2008, Definition 3.1] 3.2 total volatile organic compound (TVOC) total collection of volatile organic compounds with retention time between n-hexane and n-hexadecane when analyzed with a non-polar column (with a polarity index less than 10) [JC/T 481-2015, Definition 3.2] 3.3 waterborne floor coaling synthetic resin-based floor coating with water as the main dispersion medium 3.4 solvent-borne floor coating floor coating with volatile organic compounds, which will not become component of the coating after solidification, as dispersion medium 3.5 solvent-free floor coating floor coating with organic compounds, which will exist as film-forming substance after solidification, as dispersion medium 3.6 polymer cement floor coating floor coating formulated by adopting water-based polymer and cement-based cementitious materials, into which fillers, aggregates and other additives are added 3.7 organic crosslinking reaction polymer cement floor coating floor coating formulated by adopting multi-component reactive polymer (polyurethane) and cement-based cementitious materials, into which fillers, aggregates and other additives are added 3.8 non-organic crosslinking reaction polymer cement floor coating floor coating formulated by adopting single-component polymer (powder or emulsion) and cement-based cementitious materials, into which fillers, aggregates and other additives are added 3.9 floor coating system multi-layer flooring system with functional and decorative effects, which consists of priming coat, floating coat (optional) and top coat 3.10 light load floor coating used for ground on which passengers and non-motor vehicles and, occasionally, motor vehicles with rubber tires pass through 3.11 heavy load floor coating used for ground on which forklifts and those with hard plastic tires pass through and there is occasionally impact load 4 Classification and mark 4.1 Classification Floor coating is classified according to the following four ways: a) Floor coatings are classified according to their dispersion media into waterborne floor coaling (S), solvent-free floor coating (W), solvent-borne floor coating (R) and polymer cement floor coating (J). According to the film formation mechanism, the polymer cement floor coating is further classified into organic crosslinking reaction polymer cement floor coating and non-organic crosslinking reaction polymer cement floor coating (FJ). b) Floor coating is classified according to the coating structure into priming coat (D), floating coat (Z) and top coat (M). c) Floor coating is classified according to use place into indoor (SN) and outdoor (SW) coatings. d) Floor coating is classified according to traffic carrying capacity into light load (QZ) and heavy load (ZZ). 4.2 Mark The products are marked in the sequence of product name, standard number, dispersion medium, coating structure, use place and traffic carrying capacity. Example: Top coat of solvent-borne floor coating used for outdoor light load floor is marked as: floor coating GB/T 22374-20 ×× R M SW QZ

Foreword i 1 Scope 2 Normative references 3 Terms and definitions 4 Classification and mark 4.1 Classification 4.2 Mark 5 Requirements 5.1 Requirements for limit of harmful substances 5.2 Physical property requirements 6 Test method 6.1 Test environment 6.2 Test on limit of harmful substances 6.3 Test methods for physical property 7 Inspection rules 7.1 Inspection classification 7.2 Batching 7.3 Sampling 7.4 Judgment rules 8 Marking, packaging, transport and storage 8.1 Marking 8.2 Packaging 8.3 Transport 8.4 Storage Annex A (Normative) Determination of free 4.4'-diaminodiphenylmethane (MDA) Annex B (Normative) Determination of hot tire indentation resistance

地坪涂装材料 1范围 本标准规定了地坪涂装材料的术语和定义、分类和标记、要求、试验方法、检验规则、标志、包装、运输和贮存。 本标准适用于涂装在水泥砂浆、混凝土等基面上，对地面起装饰、保护作用以及具有特殊功能(防静电性、防滑性等）要求的合成树脂基和聚合物水泥复合地坪涂装材料。 2规范性引用文件 下列文件对于本文件的应用是必不可少的。凡是注日期的引用文件，仅注日期的版本适用于本文件。凡是不注日期的引用文件，其最新版本(包括所存的修改单）适用于本文件。 GB/T 250纺织品 色牢度试验 评定变色用灰色样卡 GB/T 1633—2000 热塑性塑料维卡软化温度(VST）的测定 GB/T 1728—1979 漆膜、腻子膜干燥时间测定法 GB/T 1731 漆膜柔韧性测定法 GB/T 1766 色漆和清漆 涂层老化的评级方法 GB/T 1768 色漆和清漆 耐磨性的测定 旋转橡胶砂轮法 GB/T 1865—2009 色漆和清漆 人工气候老化和人工辐射暴露 滤过的氙弧辐射 GB/T 2411—2008 塑料和硬橡胶 使用硬度计测定压痕硬度(邵氏硬度） GB/T 2567—2008 树脂浇铸体性能试验方法 GB/T 4100—2015 陶瓷砖 GB/T 6682 分析实验室用水规格和试验方法 GIVT 6739 色漆和清漆 铅笔法测定漆膜硬度 GB/T 8170 数值修约规则与极限数值的表示和判定 GB 8624 建筑材料及制品燃烧性能分级 GB/T 9271 色漆和清漆 标准试板 GB/T 9274—1988 色漆和清漆 耐液体介质的测定 GB 9743 轿车轮胎 GB/T 9754 色漆和清漆 不含金属颜料的色漆漆膜的20°、60°和85°镜面光泽的测定 GB/T 9779—2015 复层建筑涂料 GB/T 9780—2013 建筑涂料涂层耐沾污性试验方法 GB/T 11186.2-1989 漆膜颜色的测量方法 第二部分：颜色测量 GB 11614 平板玻璃 GB/T 13491 涂料产品包装通则 GB/T 17671 水泥胶砂强度检验方法(ISO法） GIVT 18446 色漆和清漆用漆基 异氰酸酯树脂中二异氰酸酯单体的测定 GB 18581—2009 室内装饰装修材料 溶剂型木器涂料中有害物质限量 GB 18582—2008 室内装饰装修材料 内墙涂料中有害物质限量 GB 18583—2008 室内装饰装修材料 胶粘剂中有害物质限量 GB/T 23985—2009 色漆和清漆 挥发性有机化合物(VOC）含量的测定 差值法 GB/T 23993 水性涂料中甲醛含量的测定 乙酰丙酮分光光度法 GB 24408—2009 建筑用外墙涂料中有害物质限量 GB 24613 玩具用涂料中有害物质限量 JC/T 412.1—2006 纤维水泥平板 第1部分：无石棉纤维水泥平板 JC/T 547陶瓷砖胶粘剂 JC/T 985—2017 地面用水泥基自流平砂浆 JC/T 2327—2015 水性聚氨酯地坪 JG/T 25 建筑涂料涂层耐温变性试验方法 JG/T 481—2015 低挥发性有机化合物(VOC）水性内墙涂覆材料 SJ/T 11294 防静电地坪涂料通用规范 YB/T 4086—2017 钢棉纤维 3术语和定义 GB 18582—2008、JG/T 481—2015界定的以及下列术语和定义适用于本文件。 3.1 挥发性有机化合物(VOC） volatile organic compound 在101.3 kPa标准大气压下，任何初沸点低于或等于250℃的有机化合物。 [GB 18582—2008,定义 3.1] 3.2 总挥发性有机化合物(TVOC） total volatile organic compound 用非极性色谱柱(极性指数小于10）对采集样品进行分析，保留时间在正己烷和正十六烷之间的挥发性有机化合物总和。 [JG/T 481—2015,定义 3.2] 3.3 水性地坪涂装材料 waterborne floor coaling 以水为主要分散介质的合成树脂基地面涂装类材料。 3.4 溶剂型地坪涂装材料 sol vent-borne floor coating 以具有挥发性的且固化后不能成为涂层组份的有机物为分散介质的地面涂装类材料。 3.5 无溶剂型地坪涂装材料 solvent-free floor coating 以有机物为分散介质且固化后作为成膜物质存在的地面涂装类材料。 3.6 聚合物水泥复合地坪涂装材料 polymer cement floor coating 由水性聚合物和水泥基胶凝材料为主要原料，加入填料、骨料及其他助剂配制而成的地面涂装类材料。 3.7 有机交联反应型聚合物水泥复合地坪涂装材料 organic crosslinking reaction polymer cement floor coating 由多组分反应型聚合物(聚氨酯）和水泥基胶凝材料为主要原料，加入填料、骨料及其他助剂配制而成的地面涂装类材料。 3.8 非有机交联反应型聚合物水泥复合地坪涂装材料 non-organic crosslinking reaction polymer cement floor coating 由单组份聚合物(胶粉或乳液）和水泥基胶凝材料为主要原料，加入填料、骨料及其他助剂配制而成的地面涂装类材料。 3.9 地坪涂装材料涂层体系 floor coating system 由底涂、中涂(可选）和面涂组成的具有功能性和装饰效果的多层地坪体系。 3.10 轻载地坪light load floor 用于人行交通及非机动车，偶尔有橡胶轮胎的机动车通行的地面涂装类材料。 3.11 重载地坪 heavy load floor 用于叉车及有硬塑轮胎的叉车通行，偶尔有冲击荷载的地面涂装类材料。 4分类和标记 4.1分类 地坪涂装材料按下列4种方式分类： a） 地坪涂装材料按其分散介质分为水性地坪涂装材料(S）、尤溶剂型地坪涂装材料(W）、溶剂型地坪涂裝材料(R）;聚合物水泥复合型地坪涂装材料(J）。根据成膜机理，将聚合物水泥复合型地坪涂装材料又分为：有机交联反应型聚合物水泥复合地坪涂装材料(JJ）和非有机交联反聚合物水泥复合地坪涂装材料(FJ）。 b） 地坪涂装材料按涂层结构分为：底涂(D）、中涂(Z）、面涂(M）。 c）地坪涂装材料按使用场所分为：室内(SN）和室外(SW）。 d）地坪涂装材料按交通承载量分为：轻载(QZ）、重载(ZZ）。 4.2标记 按产品名称、标准号、分散介质、涂层结构、使用场所、交通承载量的顺序标记示例： 溶剂型室外轻载地坪涂装材料面涂标记为：地坪涂装材料GB/T 22374—20×× R M SW QZ 5要求 5.1有害物质限量要求 地坪涂装材料有害物质限量应符合表1的要求。 表1地坪涂装材料有害物质限量的要求 序号 项目 指标 S型 R型 W型 J型 1 挥发性有机化合物含量(VOC）/(g/L）≤ 120 500 60 50 2 游离中醛/(mg/kg） ≤ 100 500 100 100 3 苯(g/kg） ≤ — 1 0.1 — 4 甲笨、乙苯、二甲苯的总和(g/kg） ≤ — 200 10 — 5 苯、甲苯、乙苯、二甲苯的总和/(g/kg） ≤ 5 — — 5 6 游离二异氰酸酯(TDI、HDI）a(限聚氨酯类）(g/kg）≤ 2 — 7 乙二醇醚及醚酯总和/(mg/kg） ≤ 300 8 邻苯二甲酸酯含量/% ≤ 邻苯二甲酸二异辛酯 (DEHP）、邻苯二甲酸二丁酯 (DBP）和邻苯二甲酸丁苄酯 (BBP）总和 — 0.1 — 邻苯二甲酸二异壬酯 (DINP）、邻苯二甲酸二异 酯(DIDP）和邻苯二甲酸二辛酯(DNOP）总和 — 0.1 — 9 游离4,4’-二氨基二苯中烷(MDA）b(限环氧类）/(g/kg） ≤ 10 — 10 可溶性重金属c/(mg/kg） ≤ 铅(Pb） 30 镉(Cd） 30 铬(Cr） 30 汞(Hg） 10 11 总挥发性有机化合物(TVOC）释放量b/(mg/m³） ≤ 10 商定 20 10 12 甲醛释放量b/(mg/m3） ≤ 0.1 a 单组分水性地坪涂装材料不测。 b 仅适用于室内地坪涂装材料 c 仅适用于有色地坪涂装材料。 5.2物理性能要求 5.2.1地坪涂装材料底涂 地坪涂装材料底涂应符合表2的要求。 表2地坪涂装材料底涂的要求 序号 项目 指标 S型 R型 W型 1 容器中状态 搅拌混合后均匀，无硬块 2 干燥时间/h 表干 ≤ 8 4 6 实干 ≤ 48 24 3 耐碱性(饱和Ca(OH）2，48 h） 漆膜完整，不起泡，不剥落，允许轻微变色 4 拉伸粘结强度/MPa ≥ 2.0 5.2.2地坪涂装材料中涂 地坪涂装材料中涂应符合表3的要求。 表3 地坪涂装材料中涂的要求 序号 项目 指标 S型 R型 W型 1 容器中状态 搅拌混合后均匀，无硬块 2 干燥时间/h 表干 ≤ 8 4 6 实干 ≤ 48 24 3 耐碱性(饱和Ca(OH）2,48h） 漆膜完整，不起泡，不剥落，允许轻微变色 4 抗压强度/MPa ≥ —— 45 5.2.3 地坪涂装材料面涂及涂层体系 5.2.3.1基本性能 水性、溶剂型、无溶剂型地坪涂装材料面涂的基本性能应符合表4的要求，涂层体系的基本性能应符合表4中第8项〜第13项的要求。聚合物水泥复合地坪涂装材料面涂的基本性能应符合表5的要求。 表4水性、溶剂型、无溶剂型地坪涂装材料面涂及涂层体系的基本性能要求 序号 项目 指标 S型 R型 V型 1 容器中状态 搅拌后呈均匀状态，无硬块 2 涂膜外观 表面平整、无明显可见的缩孔、浮色、发花、起皱、针孔、开裂等现象 3 干燥时间/h 表干 ≤ 8 实干 ≤ 48 4 初始流动度a/mm ≥ 140 表4 (续） 序号 项目 指标 S型 R型 W型 5 硬度 铅笔硬度(擦伤） 商定 — 邵氏硬度(D型） — 商定 6 耐磨性(750 g/500 r）/g ≤ 0.050 0.030 7 抗压强度/MPa ≥ — 45 8 拉伸粘结强度/MPa 标准条件 ≥ 2.0 浸水后 ≥ 2.0 9 耐冲击性 轻载(500 g钢球） 涂膜无裂纹、无剥落 重载(1000 g钢球） 10 防滑性(干摩擦系数） ≥ 0.50 11 耐水性(168 h） 不起泡，不剥落，允许轻微变色，2 h后恢复 12 耐化学性 耐碱性(20%NaOH，72 h） 不起泡，不剥落，允许轻微变色 耐酸性(10%H2SO4,48 h） 不起泡，不剥落，允许轻微变色 耐油性(120#溶剂油，72 h） 不起泡，不剥落，允许轻微变色 13 耐人工气候老化性b 时间商定(不低于400 h）， 不起泡、不剥落、无裂纹，粉化≤1级，变色≤2级 a仅适用于自流平地坪涂装材料。 b仅适用于室外用地坪涂装材料。 表5聚合物水泥复合地坪涂装材料面涂的基本性能要求 序号 项目 指标 JJ型 FJ型 1 容器中状态 液体组分搅拌后呈均匀状态；粉体组分应无结块 2 涂膜外观 表曲无裂纹，颜色均匀 3 可操作时间/ min 商定 — 4 尺寸变化率/% — -0.15 〜+0.15 5 初始流动度a /mm ≥ 130 6 维卡软化点b/℃ ≥ 140 — 7 抗压强度/MPa ≥ 24 h 20.0 6.0 7 d 40.0 — 28 d — 30.0 8 抗折强度/MPa ≥ 24 h 5.0 2.0 7 d 10.0 — 28 d — 7.0 表5 (续） 序号 项目 指标 JJ型 FJ型 9 耐磨性(500 g/100 r）/g ≤ 0.15 0.50 10 防滑性(干摩擦系数） ≥ 0.6 0.6 11 拉伸粘结强度/MPa ≥ 2.0 1.0 12 耐冲击性(1 000 g钢球） 表面无裂纹、无剥落 13 耐水性(168 h） 无起泡，无剥落，无裂纹， 无变色 无起泡，无剥落，无裂纹， 无变色 14 耐化学性 耐碱性 (20%NaOH,72 h） 无起泡，无剥落，无裂纹. 允许轻微变色 无起泡，无剥落，无裂纹， 允许轻微变色 耐酸性(10%H2SO4,48 h） 无起泡，无剥落，无裂纹， 允许轻微变色 — 耐油性(120#溶剂油，72 h） 无起泡，无剥落，无裂纹， 允许轻微变色 无起泡，无剥落，无裂纹， 允许轻微变色 15 耐盐水性(3%NaCl，168 h） 无起泡，无剥落，无裂纹， 允许轻微变色 无起泡，无剥落，无裂纹， 允许轻微变色 a仅适用自流平聚合物水泥复合地坪涂装材料。 b仅适用于温度高的场所。 5.2.3.2 特殊性能 特殊场合使用的地坪涂装材料面涂或涂层体系的性能除应符合表4、表5的要求外，还应符合表6 的要求。 表6地坪涂装材料面涂或涂层体系特殊性能要求 序号 项目 指标 1 高防滑性a,b 湿摩擦系数 ≥ 0.70 2 防静电性a,c 表面电阻(导静电型）/Ω ≥5×104～＜1×106 体积电阻(导静电型）/Ω 表面电阻(静电耗散型）/Ω ≥1×106～＜1×109 体积电阻(静电耗散型）/Ω 3 燃烧性能a,d 商定 4 耐特殊化学介质性a,e 商定 5 弹性f 拉伸强度/MPa ≥ 商定 断裂伸长率/% ≥ 商定 柔韧性/mm 商定   表6 (续） 序号 项目 指标 6 涂层耐温变性a,g 漆膜表面无起泡、剥落、变色等现象 7 抗划伤性h ≤ 商定 8 抗热胎压痕性a,i △E*≤3.0(单色）；变色≤1级(彩色） a 可根据有关方商定测试配套底涂后或与底涂和中涂后的性能。 b 适用于对防滑性有特殊要求的场所。 c 适用于需防静电的场所。 D 适用于对燃烧性能有要求的场所。 e 适用于需接触高浓度酸、碱、盐等化学腐蚀性药品的场所。 f 适用于弹性地坪涂装材料。 g 适用于冷库或蒸汽消毒，有温度变化差异的使用场所。 h 适用于表面光滑地坪涂装材料。 i 适用于车库、停车场等场所。 6试验方法 6.1试验环境 标准试验条件为温度(23±2）°C，相对湿度(50 ± 5）%。试样应在此条件下放置至少24 h后进行试验。 6.2 有害物质限量试验方法 6.2.1一般规定 按产品规定的配比混合后进行试验。如稀释剂的使用量为某一范围时，应按照最大稀释量稀释后进行试验。 6.2.2有害物质释放量试板制备 6.2.2.1试验基材 平板玻璃应符合GB 11614的规定。 6.2.2.2试板制备 有害物质释放量试板应符合表7的规定。 表7有害物质释放量试板制备 项目 试板类型 试件数量 块 尺寸 mm 一次涂刷 g S型、R型 W型 J型 总挥发性有机化合(TVOC） 释放量、甲醛释放量 平板玻璃 2 200×300 12.0 ± 0.2 75 ± 2 120 ± 2 6.2.3 挥发性有机化合物含量(VOC) 水性地坪涂装材料的挥发性有机化合物含量(VOC)按GB 18582-2008中附录A规定进行试验。 溶剂塑及无溶剂型地坪涂装材料的挥发性有机化合物含量(VOC)按GB/T 23985规定进行试验，并按GB/T 23985-2009中8.3式(2) 计算。将试样搅拌均匀后，称取(l.0±0.l)g试样置于盘中，溶剂型地坪涂装材料立即放入(105±2)℃高温试验箱中1h;无溶剂型地坪涂装材料在(23±2)℃、相对湿度(50±5)%条件下放置24 h后放入(105±2)℃高温试验箱中1h。 聚合物水泥复合地坪涂装材料按GB/T 23985规定进行试验•并按GB/T 23985-2009中8.4式(3)计算。 6.2.4 游离甲醛 水性地坪涂装材料的游离甲醛按GR/T 23993规定进行试验，溶剂型、无溶剂型及聚合物水泥复合地坪涂装材料的游离甲醛按GB 18583-2008中附录A中溶剂型胶粘剂的规定进行试验。 6.2.5苯及甲苯、乙苯、二甲苯的总和 水性地坪涂装材料的苯及甲苯、乙苯、二甲苯总和按GB 18582-2008中附录A进行试验。水性地坪涂装材料不稀释。 溶剂型、无溶剂型和聚合物水泥复合地坪涂装材料的苯及甲苯、乙苯、二甲苯的总和按GB 18581-2009中附录B规定进行试验。若产品规定了稀释比例或产品由双组分或多组分组时，应分别测定稀释剂和各组分中的含量，再按产品规定的配比计算混合后地坪涂装材料中的总量。如稀释剂的使用量为某一范围时，应按照推荐的最大稀释量进行计算。固体组分不测含量，仅参与计算。 6.2.6游离二异氰酸酯(TDI，HDI) 按GB/T 18446规定进行试验。若规定了稀释比例或由双组分或多组分组成时，应先测定固化剂(含有二异氰酸酯化合物）中的含量，再按产品规定的配比计算混合后地坪涂装材料中的含量。如稀释剂的使用量为某一范围时，应按照推荐的最小稀释量进行计算。固体组分不测含量，仅参与计算。 6.2.7 乙二醇醚及醚酯总和 乙二醇醚及醚酯总和为；乙二醇甲醚、乙二醇甲醚醋酸酯、乙二醇乙醚、乙二醇乙醚醋酸酯和二乙二醇丁醚醋酸酯、乙二醇丁醚、乙二醇丁醚醋酸酯的含量总和。 水性地坪涂装材料的乙二醇醚及醚酯总和按GB 24408-2009中附录A的方法进行试验。水性地坪涂装材料不稀释。 溶剂型、无溶剂型和聚合物水泥复合地坪涂装材料的乙二醇醚及醚酯总和按GB 24408-2009中附录D的方法进行试验。若产品规定了稀释比例或产品由双组分或多组分组成时.，应分别测定稀释剂和各组分中的含量，再按产品规定的配比计算混合后地坪涂装材料中的总量。如稀释剂的使用量为某一范围时，应按照推荐的最大稀释量进行计算。固体组分不测含量，仅参与计算。 6.2.8 邻苯二甲酸酯含量 按GB 24613规定进行。 6.2.9 游离4.4'-二氨基苯甲烷(MDA) 按附录A规定进行试验，以固化剂中的含量报出。 6.2.10 可溶性重金属 按GB 18582-2008中附录D规定进行。 6.2.11 总挥发性有机化合物(TVOC)释放量、甲醛释放量 按JG/T 481-2015中7.3规定进行。 6.3 物理性能试验方法 6.3.1 试验样板制备 6.3.1.1试验基材 6,3.1.1.1 无石棉纤维水泥平板应符合JC/T 412.1-2006中厚度为4mm〜6 mm的NAF H V级板的规定。 6.3.1.1.2 马口铁板、钢板、铝板或玻璃板的材质要求及处理应符合GB/T 9271的规定。 6.3.1.1.3 混凝土板应符合JC/T 547的规定。 6.3.1.2 试样制备 6.3.1.2.1 地坪涂装材料制板的要求 将地坪涂装材料各组份按产品说明书提供的使用比例混合，若给出一个值域范围，则取中间值。 将试样混合并揽拌均匀，以产品说明书提供的施工方法将试样涂布于符合6.3.1.1规定的试验基材表面，如没有特别规定则采用空气喷涂法或刷涂法制板。 需进行多道涂装或涂层体系制备时按产品说明书进行。如没有特别规定按表8、表9的要求进行制备和养护，涂装间隔为24h。制备好的试板和试件的表面应平整、无裂纹。