标准编号:	JG/T 161-2016
中文名称:	无粘结预应力钢绞线
英文名称:	Unbonded prestressing steel strand
中标分类:	P27    组合结构工程
行业分类:	JG    建筑工业行业标准
ICS分类:	91.100.30 91.100.30    混凝土和混凝土制品 91.100.30
发布机构:	中华人民共和国住房和城乡建设部
发布日期:	2016-11-15
实施日期:	2017-5-1
标准状态:	valid
替代旧标准:	JG 161-2004 无粘结预应力钢绞线
翻译语言:	英文
文件格式:	PDF
中文字符数:	15000 字
翻译价格(元):	816.0
交付时间:	付款后 1 个工作日

Foreword Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed in accordance with the rules given in GB/T 1.1-2009. This standard replaces JG/T 161-2004 Unbonded prestressing steel strand, and the following main technical changes have been made with respect to JG/T 161-2004: ——Terms and definitions and symbols have been modified (see Clause 3 hereof; Clause 3 of Edition 2004); ——The clause "General requirements" has been added (see Clause 5 hereof); ——"Materials" has been deleted (see 5.1 of Edition 2004); ——Requirements for anticorrosion lubricating coating have been modified, (see 6.4 hereof; 5.1.2 of Edition 2004); ——Sheathing properties and test method have been modified (see 6.5 and 7.4 hereof; 5.1.3 and 6.3 of Edition 2004); ——Value and test method of the friction coefficient have been modified (see 6.6 and Annex B hereof; 5.2 and 6.4 of Edition 2004); ——The inspection classification has been modified (see 8.1 hereof; 7.1 of Edition 2004); ——Inspection items have been modified (see 8.2 hereof; 7.2 of Edition 2004); ——The rules of raw material batching, sampling and judgment have been deleted (see 7.3 of Edition 2004); ——The rules of batching, sampling and judgment have been modified (see 8.3 hereof; 7.4 of Edition 2004); ——The storage has been modified (see 10.2 hereof; 8.4 of Edition 2004); ——The original annex "Acceptance and application instructions" has been deleted (see Annex A of Edition 2004); ——The annex "Test method for tensile properties of sheathing" has been added (see Annex A hereof). This standard was proposed by the Research Institute of Standards and Norms of Ministry of Housing and Urban-Rural Development. This standard is under the jurisdiction of the Technical Committee of Standardization Administration of the Ministry of Housing and Urban-Rural Development. The previous editions of this standard are as follows: ——JG 3006-1993; ——JG 161-2004. Unbonded prestressing steel strand 1 Scope This standard specifies the terms and definitions, symbols and designation, general requirements, requirements, test methods, inspection rules, marking, packaging, quality certificate, transportation and storage of unbonded prestressing steel strand. This standard is applicable to unbonded prestressing steel strands used in post-tensioned prestressing concrete structures. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 5224 Steel strand for prestressed concrete GB/T 11115 Polyethylene(PE) resin GB/T 17200 Technical specification for tensile compression and flexural testing machines for rubber and plastics (constant rate of traverse) JG/T 430 Anticorrosion lubricating grease for unbonded tendons 3 Terms, definitions and symbols For the purposes of this document, the following terms and definitions apply. 3.1 Terms and definitions 3.1.1 unbonded prestressing steel strand prestressing steel strand coated with anticorrosion lubricating coating, enveloped by sheathing, which can slide permanently against sheathing 3.1.2 prestressing steel strand steel strand twisted from cold drawn round wire 3.1.3 anticorrosion lubricating coating coating applied to the surface of prestressing steel strand to prevent corrosion and reduce friction between steel strand and sheathing. 3.1.4 sheathing sleeve wrapped around a prestressing steel strand and an anticorrosion lubricating coating to protect the prestressing steel strand from corrosion and to prevent bonding with surrounding concrete 3.1.5 tensile stress at yield initial stress, from which the specimen stress does not increase but the strain increases in the tensile process 3.1.6 nominal tensile strain at break increment of the original length of the distance between the two fixtures when the specimen breaks after yielding during stretching, expressed as a percentage (%) 3.2 Symbols κ——considering the influence coefficient of local deviation of sheath wall (per meter) of unbonded prestressing steel strand on friction; μ——friction coefficient between steel strand and sheathing wall in unbonded prestressing steel strand. 4 Designation The designation of unbonded prestressing steel strand consists of product name code, nominal diameter of steel strand, nominal tensile strength of steel strand and standard number: Examples: Unbonded prestressing steel strands with nominal diameter of 15.20 mm and nominal tensile strength of 1860 MPa shall be designated as: UPS 15.20 1860 JG/T 161 2016

Foreword i 1 Scope 2 Normative references 3 Terms, definitions and symbols 4 Designation 5 General requirements 6 Requirements 7 Test methods 8 Inspection rules 9 Marking, packaging and quality certification documents 10 Transportation and storage Annex A (Normative) Test method for tensile properties of sheathing Annex B (Normative) Test method for determination of friction coefficient

ICS 91.100.30 P 27 JG 中华人民共和国建筑工业行业标准 JG/T 161—2016 代替JG 161—2004 无粘结预应力钢绞线 Unbonded prestressing steel strand 2016-11-15发布 2017-05-01实施 中华人民共和国住房和城乡建设部 发布 前言 本标准按照GB/T 1.1—2009给出的规则起草。 本标准代替JG/T 161—2004《无粘结预应力钢绞线》，与JG 161—2004相比，主要技术内容变化如下： ——修改了术语和定义、符号(见3，2004年版的3)； ——增加了“一般要求”(见5)； ——删除了“材料”(见2004年版的5.1)； ——修改了防腐润滑涂层的要求(见6.4，2004年版的5.1.2)； ——修改了护套的性能和试验方法(见6.5和7.4，2001年版的5.1.3和6.3)； ——修改了摩擦系数的取值和试验方法(见6.6和附录B，2004年版的5.2和6.4)； ——修改了检验分类(见8.1，2004年版的7.1)； ——修改了检验项目(见8.2，2004年版的7.2)； ——删除了原材料组批、抽样及判定规则(见2004年版的7.3)； ——修改了组批、抽样及判定规则(见8.3，2004年版的7.4)； ——修改了贮存(见10.2，2004年版的8.4)； ——删除了附录“进场验收及应用说明”(见2004年版的附录A)； ——增加了附录“护套拉伸性能试验方法”(见附录A)。 本标准由住房和城乡建设部标准定额研究所提出。 本标准由住房和城乡建设部建筑结构标准化技术委员会归口。 本标准所代替标准的历次版本发布情况为： ——JG 3006—1993； ——JG 161—2004。 无粘结预应力钢绞线 1 范围 本标准规定了无粘结预应力钢绞线的术语和定义、符号、标记、一般要求、要求、试验方法、检验规则、标志、包装及质量证明文件、运输和贮存。 本标准适用于后张预应力混凝土结构中使用的无粘结预应力钢绞线。 2 规范性引用文件 下列文件对于本文件的应用是必不可少的。凡是注日期的引用文件，仅注日期的版本适用于本文件。凡是不注日期的引用文件，其最新版本(包括所有的修改单)适用于本文件。 GB/T 5224 预应力混凝土用钢绞线 GB/T 11115 聚乙烯(PE)树脂 GB/T 17200 橡胶塑料拉力、压力和弯曲试验机(恒速驱动) 技术规范 JG/T 430 无粘结预应力筋用防腐润滑脂 3 术语和定义、符号 下列术语和定义、符号适用于本文件。 3.1 术语和定义 3.1.1 无粘结预应力钢绞线 unbonded prestressing steel strand 表面涂敷防腐润滑涂层，外包护套，与护套之间可永久相对滑动的预应力钢绞线。 3.1.2 预应力钢绞线 prestressing steel strand 由冷拉光圆钢丝捻制的钢绞线。 3.1.3 防腐润滑涂层 anticorrosion lubricating coating 涂敷于预应力钢绞线表面，用以防腐和减小钢绞线与护套之间摩擦的涂层。 3.1.4 护套 sheathing 包裹在预应力钢绞线和防腐润滑涂层外，用以保护预应力钢绞线不受腐蚀，并防止其与周围混凝土之间发生粘结的套管。 3.1.5 拉伸屈服应力 tensile stress at yield 拉伸过程中，试样出现应力不增加而应变增加时的最初应力。 3.1.6 拉伸断裂标称应变 nominal tensile strain at break 拉伸过程中，试样在屈服后断裂时，两夹具之间距离单位原始长度的增量，用百分数(％)表示。 3.2 符号 κ——考虑无粘结预应力钢绞线护套壁(每米)局部偏差对摩擦的影响系数； μ——无粘结预应力钢绞线中钢绞线与护套壁之间的摩擦系数。 4 标记 无粘结预应力钢绞线的标记由产品名称代号、钢绞线的公称直径、钢绞线的公称抗拉强度和标准号组成： JG/T 161—2016 钢绞线的公称抗拉强度，单位为兆帕(MPa) 钢绞线的公称直径，单位为毫米(mm) UPS：无粘结预应力钢绞线代号 示例： 公称直径为15.20mm，公称抗拉强度为1860MPa的无粘结预应力钢绞线标记为： UPS15.20 1860 JG/T 161 2016 5 一般要求 5.1 预应力钢绞线、防腐润滑涂层材料和护套材料应经检验合格后方可用于制作无粘结预应力钢绞线。 5.2 防腐润滑涂层材料的涂敷及护套的制作应一次连续完成，护套制作应采用挤塑机挤出成型。 5.3 每盘无粘结预应力钢绞线应由一根连续的钢绞线组成，不应有死弯。 5.4 无粘结预应力钢绞线生产厂应具备完整的可追溯性质量管理体系文件，其内容应包括：原材料采购及检验记录、生产工艺、生产过程记录、产品检验记录。 5.5 当用于体外预应力时，宜根据使用要求对无粘结预应力钢绞线采取有效的防护措施。 6 要求 6.1 规格和性能 无粘结预应力钢绞线的主要规格和性能应符合表1的规定。 表1 无粘结预应力钢绞线的规格和性能 钢绞线 防腐润滑脂的含量 g/m 护套厚度 mm κ μ 公称直径 mm 公称横截面积 mm2 公称抗拉强度 MPa 9.50 54.80 1720 ≥32 ≥1.0 ≤0.004 ≤0.09 1860 1960 12.70 98.70 1720 ≥43 ≥1.0 ≤0.004 ≤0.09 1860 1960 15.20 140.00 1720 ≥50 ≥1.0 ≤0.004 ≤0.09 1860 1960 15.70 150.00 1720 ≥53 ≥1.0 ≤0.004 ≤0.09 1860 1960 注：经供需双方协商，也可生产供应其他强度和直径的无粘结预应力钢绞线。 6.2 外观 无粘结预应力钢绞线的护套表面应光滑、无凹陷、无可见钢绞线轮廓、无气孔、无机械损伤、无裂缝、无明显折皱。 6.3 钢绞线 6.3.1 钢绞线应符合GB/T 5224或国家现行其他类型钢绞线相关标准的规定，钢绞线生产厂应提供质量证明文件及检测报告。 6.3.2 钢绞线在运输和贮存期间应进行妥善防腐保护，涂油包塑前其表面不应锈蚀及沾染腐蚀介质或其他杂物。 6.4 防腐润滑涂层 6.4.1 防腐润滑涂层应具有良好的化学稳定性，对周围材料无侵蚀作用，能阻水防潮和抗腐蚀，润滑性能好，在规定温度范围内高温不流淌，低温不变脆。 6.4.2 宜采用防腐润滑脂制作防腐润滑涂层，防腐润滑脂应符合JG/T 430的规定，防腐润滑脂生产厂应提供质量证明文件及检测报告。 6.4.3 防腐润滑脂应沿钢绞线全长连续涂敷并充足饱满，防腐润滑脂的含量应符合表1的规定。 6.4.4 当需方有要求时，也可采用其他材料作为防腐润滑涂层，涂层材料的性能应符合JG/T 430或其他国家现行标准的规定。 6.5 护套 6.5.1 应采用密度在0.942g/cm3～0.965g/cm3范围内的高密度聚乙烯树脂制作护套，性能应符合GB/T 1115的规定。护套原料生产厂应提供质量证明文件及检测报告。 6.5.2 护套原料中不应掺加其他影响护套性能的填充料。 6.5.3 护套颜色宜根据需方要求确定，但添加了色母料的护套应满足护套性能的要求。 6.5.4 无粘结预应力钢绞线的护套厚度应均匀，并符合表1的规定。 6.5.5 护套的拉伸性能应符合表2的规定。 表2 护套的拉伸性能 拉伸屈服应力/MPa 拉伸断裂标称应变/％ ≥15 ≥400 6.6 摩擦系数 6.6.1 κ和μ应符合表1的规定。 6.6.2 当κ＜0.003或μ＜0.04时，生产厂应提供κ和μ的实测数值。 6.6.3 表1中未列出规格的无粘结预应力钢绞线的κ和μ应根据实测数据确定。