标准编号:	GB/T 2057-1989
中文名称:	镍阳极板
英文名称:	Nickel anode sheets
行业分类:	GB    国家标准
发布日期:	1990-03-01
实施日期:	1990-3-1
标准状态:	superseded
被新标准替代:	GB/T 2056-2005 电镀用铜、锌、镉、镍、锡阳极板
被替代日期:	2006-1-1
翻译语言:	英文
文件格式:	PDF
中文字符数:	3000 字
翻译价格(元):	300.0
交付时间:	付款后 1 个工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. Nickel Anode Sheets 1 Subject content and applicable scope This standard specifies the product classification, technological requirements, test methods, inspection rules, and packaging of nickel anode sheets. This standard is applicable to nickel anode sheets for electroplating in industry sector. 2 Normative references GB 5235 Wrought nickels and nickel alloys—Chemical composition and forms of wrought products GB/T 8647 Methods for chemical analysis of nickel GB 8888 Wrought heavy non-ferrous metal products—Packing, marking, transporting and storing 3 Product classification 3.1 Designation, temper and specification The designation, temper and specification of the sheets shall meet those specified in Table 1. Table 1 Designation Temper Thickness mm Width mm Length mm NY1 Hot-rolled (R) 6~20 100~300 400~2,000 NY3 Soft (M) 4~20 NY2 Hot-rolled before quenched (C) 3.2 Overall dimension and allowable deviation 3.2.1 The overall dimension and allowable deviation of the NY1 and NY3 sheets, and the thickness of the NY2 sheets (±10 mm for width deviation, ±35 mm for length deviation) shall meet those specified in Table 2. Table 2 In: mm Thickness Width Length Basic dimension Allowable deviation Basic dimension Allowable deviation Basic dimension Allowable deviation 4~5 ±0.40 >5~10 ±0.50 100~300 ±5 400~2,000 ±20 >10~14 ±0.60 >14~20 ±0.80 To be supplied untrimmed To be supplied untrimmed Note: 1. The width of the sheets is graded according to 50 mm and the length is graded according to 200 mm. 2. Sheets of other specification and allowable deviation may be supplied by mutual agreement between the supplier and the purchaser. 3. The thickness of the NY2 sheets to be supplied shall not be less than 6 mm. 3.2.2 The sheets shall be flat and straight in shape, and the uneven part along the length of the sheets shall not exceed 50 mm per meter. 3.2.3 For NY1 and NY3 sheets with thickness less than or equal to 14 mm, the edges shall be cut straight and free of cracks, while slight burr is allowed; oblique cutting shall not make the width and the length of the sheets exceed the allowable deviation. For NY2 sheets, the edges and the head shall not be cut for the purpose of supply, and the edges may be allowed to have cracks when the sheets are within the range of the allowable width and length deviation. 3.3 Designation example For NY2 sheets that has been tempered, 10 mm in thickness, 300 mm in width, and 1,000 mm in length, the designation is as follows: Sheet NY2 C 10×300×1,000 GB 2057-89 4 Technical requirements 4.1 Chemical composition The chemical composition of the nickel anode sheets shall meet the requirements of GB 5235. 4.2 Surface quality 4.2.1 The sheets need no acid cleaning for the purpose of supply. It is not allowed to have bubbles, peeling and inclusions on the surface. 4.2.2 Slight defects, such as bumps, pits and roller marks, that do not make the thickness of the sheets exceed the allowable deviation are allowed on the surface of the sheets. 4.2.5 No cracks are allowed on the surface of NY1 and NY3 sheets, but slight delamination caused by shearing is allowed at the cut. The surface of NY2 sheets is allowed to have slight cracks that do not make the thickness of the sheets exceed the allowable deviation. 5 Test methods 5.1 The arbitration analysis method for chemical compositions of nickel anode sheets shall be in accordance with YB 128. 5.2 The overall dimension of sheets shall be measured by measuring tool with corresponding precision. 5.3 The surface quality of the sheets shall be visually inspected. 6 Inspection rules 6.1 Inspection and acceptance 6.1.1 The sheets shall be subjected to the technical supervision department of the supplier for acceptance and to guarantee that the quality meets the requirements of this standard. 6.1.2 The purchaser shall test the received products according to those specified hereof; if the test result is inconsistent with specifications in this standard, the condition shall be proposed to the supplier within 3 months from the day of receiving the products, and solved by consultation between the supplier and the purchaser.

1 Subject content and applicable scope 2 Normative references 3 Product classification 4 Technical requirements 5 Test methods 6 Inspection rules 7 Packaging, marking, transportation and storage

中华人民共和国国家标准 GB 2057—89 镍阳极板 代替GB 2057—80 Nickel anode sheets _____________________________________________________________________________ 中国有色金属工业总公司1989-02-25批准 1990-03-01实施 1 主题内容与适用范围 本标准规定了镍阳极板的产品分类、技术要求、试验方法、检验规则和包装等。 本标准适用于工业部门电镀用的镍阳极板。 2 引用标准 GB 5235 加工镍及镍合金 化学成分和产品形状 GB 8647 镍化学分析方法 GB 8888 重有色金属加工产品包装、标志、运输和贮存 3 产品分类 3.1 牌号、状态、规格 板材的牌号、状态和规格应符合表1的规定。 表1 牌号 状态 厚度 mm 宽度 mm 长度 mm NY1 热轧(R) 6～20 100～300 400～2 000 NY3 软(M) 4～20 NY2 热轧后淬火(C) 3.2 外形尺寸及允许偏差 3.2.1 NY2板材的宽度允许偏差为±10 mm，长度允许偏差为±35 mm，厚度及其允许偏差和NY1、NY3板材的外形尺寸及其允许偏差应符合表2的规定。 表2 mm 厚度 宽度 长度 基本尺寸 允许偏差 基本尺寸 允许偏差 基本尺寸 允许偏差 4～5 ±0.40 ＞5～10 ±0.50 100～300 ±5 400～2 000 ±20 ＞10～14 ±0.60 ＞14～20 ±0.80 不切边供应 不切头供应 注：① 板材的宽度按50 mm进级、长度按200 mm进级。 ② 经供需双方协议，可供应其他规格和允许偏差的板材。 ③ NY2供货厚度规格从6 mm开始。 3.2.2 板材外形应平直，其长度方向的不平度每米不超过50 mm。 3.2.3 厚度小于和等于14 mm的NY1、NY3板的边应切直、无裂边；允许有轻微的毛刺；切斜不应使板材宽度和长度超出其允许偏差。 NY2板的边部和头部不经剪切供应。在宽度及长度允许偏差范围内，边部允许有裂口。 3.3 标记示例 用NY2制造的淬火状态、厚度为10 mm、宽度为300 mm、长度为1 000 mm的板材，标记为： 板NY2 C 10×300×1 000 GB 2057—89 4 技术要求 4.1 化学成分 板材的化学成分应符合GB 5235的规定。 4.2 表面质量 4.2.1 板材不经酸洗供应，表面不允许有气泡、起皮和夹杂。 4.2.2 板材表面允许有轻微的、不使板材厚度超出其允许偏差的凸点、凹坑和辊印等缺陷。 4.2.5 NY1和NY3板的表面不允许有裂纹，但其切口处允许有剪切时产生的轻微的分层现象。 NY2板的表面允许有轻微的，不使板材厚度超出其允许偏差的小裂纹。 5 试验方法 5.1 板材的化学成分仲裁分析方法按YB 128的规定进行。 5.2 板材外形尺寸用相应精度的测量工具进行测量。 5.3 板材的表面质量用目视进行检查。 6 检验规则 6.1 检查和验收 6.1.1 板材应由供方技术监督部门验收，并保证产品质量符合本标准要求。 6.1.2 需方对收到的产品应按本标准的规定进行重复试验，如果复验结果与本标准规定不符时，应在收到产品之日起三个月内向供方提出，由供需双方协商解决。 6.2 组批 板材应成批提交验收，每批板材应由同一牌号、厚度规格、制造方法、状态所组成，其批重不大于2t。 6.3 检验项目 每批板材均应进行化学成分、外形尺寸和表面质量的检验。 6.4 取样位置和取样数量 6.4.1 供方在熔铸过程中，每炉取一个试样进行化学成分的检验。 6.4.2 需方在每批板材中任取一个试样进行化学成分的检验。 6.4.3 板材厚度在距顶角不小于100 mm和距边部不小于10 mm处测量，测量范围以外的厚度超差不作报废依据。 6.4.4 板材应逐张进行外形尺寸测量和表面质量的检验。 6.5 重复试验 化学成分检验结果不合格时，应从该批中再取双倍试样进行复验，复验结果仍有一个试样不合格，则整批报废。 7 包装、标志、运输和贮存 包装、标志、运输和贮存按GB 8888的规定进行。