标准编号:	GB/T 2072-2020
中文名称:	镍及镍合金带、箔材
英文名称:	Nickel and nickel alloy strip and foil
中标分类:	H62    重金属及其合金
行业分类:	GB    国家标准
ICS分类:	77.150.40 77.150.40    镍和铬产品 77.150.40
发布机构:	国家市场监督管理总局 国家标准化管理委员会
发布日期:	2020-09-29
实施日期:	2021-8-1
标准状态:	valid
替代旧标准:	GB/T 2072-2007 镍及镍合金带材
翻译语言:	英文
文件格式:	PDF
中文字符数:	11000 字
翻译价格(元):	550.0
交付时间:	付款后 1 个工作日

Codeofchina.com is in charge of this English translation. In case of any doubt about the English translation, the Chinese original shall be considered authoritative. This standard is developed in accordance with the rules given in GB/T 1.1-2009. This standard replaces GB/T 2072-2007 Nickel and nickel alloy strips. In addition to editorial changes, the following main technical changes have been made with respect to GB/T 2072-2007: ——the grades and technical requirements of nickel foils are added (see Clauses 3 and 4); ——the specification range is modified: the thickness is changed from "0.05~1.2" to "0.01~5.00", and the width is changed from "20~250" to "20~1,350" (see Table 1; Table 1 of Edition 2007); ——the thickness, width and their tolerances are modified: the width tolerance of products with thickness not greater than 0.3mm is changed from "(0, -0.6), (0, -1.0)" to "±0.15"; the width tolerance of products with thickness greater than 0.3mm is changed from "(0, -1.0), (0, -1.5)" to "(+1.6, 0)" (see Table 2; Table 2 of Edition 2007); ——the cupping test method is modified: the punch diameter of cupping test is changed from "10mm" to "20mm" (see 5.4.1; 4.3 of Edition 2007); ——the bending property requirements for products are added (see 4.4.2); ——the grain size requirements for products are added (see 4.5). This standard was proposed by China Nonferrous Metals Industry Association. This standard is under the jurisdiction of National Technical Committee on Nonferrous Metals of Standardization Administration of China (SAC/TC 243). The previous editions of this standard are as follows: ——GB/T 2072-1980, GB/T 2072-1993 and GB/T 2072-2007; ——GB/T 11088-1989. Nickel and nickel alloy strip and foil 1 Scope This standard specifies the classification and labeling, technical requirements, test methods, inspection rules, marking, packaging, transportation and storage, as well as quality certificates and order form (or contract) contents of nickel and nickel alloy strip and foil. This standard is applicable to nickel and nickel alloy strip and foil used in industrial fields such as instruments, communications and electronics. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. GB/T 228.1-2010 Metallic materials - Tensile testing - Part 1: Method of test at room temperature GB/T 232 Metallic materials - Bend test GB/T 4156 Metallic materials - Sheet and strip - Erichsen cupping test GB/T 4340.1 Metallic materials - Vickers hardness test - Part 1: Test method GB/T 5235 Wrought nickel and nickel alloys - Chemical composition and forms of wrought products GB/T 6394 Determination of estimating the average grain size of metal GB/T 8170 Rules of rounding off for numerical values & expression and judgment of limiting values GB/T 8647 (All parts) The methods for chemical analysis of nickel GB/T 8888 Wrought heavy non-ferrous metal products - Packing, marking, transportation, storing and certificate of quality YS/T 325 (All parts) Methods for chemical analysis of nickel-copper alloy 3 Classification and labeling 3.1 Product classification Grade, variety, condition and specification of the product shall meet those specified in Table 1.   Table 1 Grade, variety, condition and specification of the product Grade Variety Condition Specification mm Thickness Width Length N2, N4, N5, N6, N7 and N8 Foil Hard (Y) 0.01~0.02 20~200 — Hard (Y), soft (M) >0.02~0.25 20~300 — N4, N5, N6, N7, NMg0.1, DN, NS10.19, NCu40-2-1, NCu28-2.5-1.5, NW4-0.15, NW4-0.1, NW4-0.07 and NCu30 Strip Hard (Y) Semi-hard (Y2) Soft (M) >0.25~0.30 20~300 ≥3,000 >0.30~0.80 20~1,100 ≥5,000 >0.80~5.00 20~1,350 ≥5,000 3.2 Product labeling A product shall be labeled in the order of product name, standard number, grade, condition and specification. Example 1: A 0.03mm×100mm (thickness × width) hard foil made of N2 material with a general precision shall be labeled as follows: Nickel foil GB/T 2072-N2Y-0.03×100 Example 2: A 1.00mm×1,000mm (thickness × width) soft strip made of N6 material with a high precision shall be labeled as follows: Nickel strip GB/T 2072-N6M high-1.00×1,000 4 Technical requirements 4.1 Chemical composition Chemical composition of each grade of product shall meet the requirements of GB/T 5235. 4.2 Overall dimension and its tolerance 4.2.1 The thickness and width as well as their tolerances of the product shall meet those specified in Table 2.   Table 2 Thickness and width as well as their tolerances of the product In mm 4.2.2 The side curvature of the product shall not be greater than 3mm/m. 4.2.3 The product shall be straight, with both sides cut neatly and be free of crack and crimp. 4.3 Mechanical properties 4.3.1 The results of tensile tests at room temperature for strips shall meet those specified in Table 3.

Foreword i 1 Scope 2 Normative references 3 Classification and labeling 4 Technical requirements 5 Test methods 6 Inspection rules 7 Marking, packaging, transportation, storage and quality certificate 8 Order (or contract) contents

ICS 77.150.40 H 62 GB 中华人民共和国国家标准 GB/T 2072—2020 代替GB/T 2072—2007 镍及镍合金带、箔材 Nickel and nickel alloy strip and foil 2020-09-29发布 2021-08-01实施 国家市场监督管理总局 国家标准化管理委员会 发布 前言 本标准按照GB/T 1.1—2009给出的规则起草。 本标准代替GB/T 2072—2007《镍及镍合金带材》，与GB/T 2072—2007相比，除编辑性修改外主要技术变化如下： ——增加了镍箔材的牌号及技术要求(见第3章、第4章)； ——修改了规格范围：厚度由“0.05～1.2”修改为“0.01～5.00”，宽度由“20～250”修改为“20～1 350”(见表1，2007年版的表1)； ——修改了厚度、宽度及其允许偏差：厚度不大于0.3 mm产品的宽度允许偏差由“(0，－0.6)、(0，－1.0)”修改为“±0.15”；厚度大于0.3 mm产品的宽度允许偏差由“(0，－1.0)、(0，－1.5)”修改为“(＋1.6，0)”(见表2，2007年版的表2)； ——修改了杯突试验方法：将杯突试验的冲头直径由“10 mm”修改为“20 mm”(见5.4.1，2007年版的4.3)； ——增加了产品的弯曲性能要求(见4.4.2)； ——增加了产品的晶粒度要求(见4.5)。 本标准由中国有色金属工业协会提出。 本标准由全国有色金属标准化技术委员会(SAC/TC 243)归口。 本标准所代替标准的历次版本发布情况为： ——GB/T 2072—1980、GB/T 2072—1993、GB/T 2072—2007； ——GB/T 11088—1989。 镍及镍合金带﹑箔材 1 范围 本标准规定了镍及镍合金带、箔材的分类和标记、技术要求、试验方法、检验规则和标志、包装、运输、贮存及质量证明书与订货单(或合同)内容。 本标准适用于仪表、通信及电子等工业领域用镍及镍合金带、箔材。 2 规范性引用文件 下列文件对于本文件的应用是必不可少的。凡是注日期的引用文件，仅注日期的版本适用于本文件。凡是不注日期的引用文件，其最新版本(包括所有的修改单)适用于本文件。 GB/T 228.1—2010 金属材料 拉伸试验 第1部分：室温试验方法 GB/T 232 金属材料 弯曲试验方法 GB/T 4156 金属材料 薄板和薄带 埃里克森杯突试验 GB/T 4340.1 金属材料 维氏硬度试验 第1部分：试验方法 GB/T 5235 加工镍及镍合金 化学成分和产品形状 GB/T 6394 金属平均晶粒度测定方法 GB/T 8170 数值修约规则与极限数值的表示和判定 GB/T 8647(所有部分) 镍化学分析方法 GB/T 8888 重有色金属加工产品包装、标志、运输、贮存和质量证明书 YS/T 325(所有部分) 镍铜合金化学分析方法 3 分类和标记 3.1 产品分类 产品的牌号、品种、状态和规格应符合表1的规定。 表1 产品的牌号、品种、状态和规格 牌号 品种 状态 规格 mm 厚度 宽度 长度 N2、N4、N5、N6、N7、N8 箔材 硬态(Y) 0.01～0.02 20～200 — 硬态(Y)、软态(M) ＞0.02～0.25 20～300 — N4、N5、N6、N7、NMg0.1、DN、NS10.19、NCu40－2－1、NCu28－2.5－1.5、NW4－0.15、NW4－0.1、NW4－0.07、NCu30 带材 硬态(Y) 半硬态(Y2) 软态(M) ＞0.25～0.30 20～300 ≥3 000 ＞0.30～0.80 20～1100 ≥5 000 ＞0.80～5.00 20～1350 ≥5 000 3.2 产品标记 产品标记按产品名称、标准编号、牌号、状态、规格的顺序表示。 示例1：用N2牌号制造的、状态为硬态、厚度为0.03 mm、宽度为100 mm的普通精度箔材，标记为： 镍箔 GB／T 2072－N2Y－0.03×100 示例2：用N6牌号制造的、状态为软态、厚度为1.00 mm、宽度为1 000 mm的高精度带材，标记为： 镍带 GB／T 2072－N6M高－1.00×1 000 4 技术要求 4.1 化学成分 产品各牌号的化学成分应符合GB／T 5235的规定。 4.2 外形尺寸及其允许偏差 4.2.1 产品的厚度、宽度及其允许偏差应符合表2的规定。 表2 产品的厚度、宽度及其允许偏差 单位为毫米 厚度 规定宽度范围的厚度允许偏差 规定宽度范围的宽度允许偏差 20～300 ＞300 20～300 ＞300 普通级 高精级 普通级 高精级 4.2.2 产品的侧边弯曲度应不大于3 mm／m。 4.2.3 产品应平直，两边切齐、无裂边和卷边。 4.3 力学性能 4.3.1 带材的室温拉伸试验结果应符合表3的规定。 表3 带材的室温拉伸试验结果 牌号 厚度mm 状态 抗拉强度Rm MPa 规定塑性延伸强度RP0.2 MPa 断后伸长率％ A11.3 A50 mm a 规定塑性延伸强度不适用于厚度小于0.5 mm的产品。 实测 4.3.2 箔材的维氏硬度应符合表4的规定。带材如有维氏硬度要求时，供需双方协商确定。 表4 箔材的维氏硬度 牌号 厚度mm 状态 维氏硬度HV 4.4 工艺性能 4.4.1 杯突试验 软态(M)产品应进行杯突试验，试验结果应符合表5的规定。其中，NCu28-2.5-1、NCu40-2-1、NCu30杯突试验结果报实测。 表5 杯突试验 单位为毫米 厚度 0.10～0.20 ＞0.20～0.55 ＞0.55～2.00 杯突值 ≥7.5 ≥8.0 ≥8.5 4.4.2 弯曲试验 产品可进行弯曲试验，弯曲后带材外表面应无裂纹，弯曲压头直径和弯曲角由供需双方协商。 4.5 晶粒度 产品可进行晶粒度检测，检测结果报实测值。 4.6 表面质量 产品表面应光滑、清洁，不准许有影响使用的缺陷。 5 试验方法 5.1 化学成分 产品的化学成分分析方法按GB／T 8647、YS／T 325的规定进行。 5.2 外形尺寸及其允许偏差 产品的外形尺寸及其允许偏差用相应精度的量具进行测量。厚度在距端部不小于100 mm和距边部不小于5 mm处测量(宽度小于50 mm的产品在距边部不小于3 mm处测量)。 5.3 力学性能 5.3.1 产品的拉伸试验按GB／T 228.1—2010的规定进行，选取P04试样或P5试样。 5.3.2 产品的维氏硬度试验按GB／T 4340.1的规定进行。 5.4 工艺性能 5.4.1 产品的杯突试验按GB／T 4156的规定进行，冲头直径为20 mm。 5.4.2 产品的弯曲试验按GB／T 232的规定进行。 5.5 晶粒度 产品的晶粒度按GB／T 6394进行检验。 5.6 表面质量 产品的表面质量用目视进行检验。 6 检验规则 6.1 检查和验收 6.1.1 产品应由供方进行检验，保证产品质量符合本标准及订货单(或合同)的规定，并填写质量证明书。 6.1.2 需方应对收到的产品按本标准的规定进行复验。复验结果与本标准及订货单(或合同)的规定不符时，应以书面形式向供方提出，由供需双方协商解决。属于外形尺寸及表面质量的异议，应在收到产品之日起一个月内提出，属于其他性能的异议，应在收到产品之日起三个月内提出。如需仲裁，应由供需双方协商确定。 6.2 组批 产品应成批提交验收，每批应由同一牌号、状态和规格的产品组成。箔材每批重量不大于500 kg，带材每批重量不大于2 000 kg。 6.3 检验项目 每批产品的检验项目应符合表6的规定。 表6 检验项目 检验项目 出厂检验项目 化学成分 √ 外形尺寸及其允许偏差 √ 力学性能 室温拉伸试验 √ 维氏硬度 √ 工艺性能 杯突试验 √ 弯曲试验 × 晶粒度 × 表面质量 √ 注：表中“√”表示“出厂检验项目”；“×”表示“需方有要求时进行的检验项目”。 6.4 取样 每批产品的取样应符合表7的规定。 表7 取样 检验项目 取样 要求的章条号 试验方法的章条号 化学成分 每批取1个试样，允许供方以原铸锭或坯料的分析结果报出 4.1 5.1 外形尺寸及其允许偏差 逐卷 4.2 5.2 力学性能 室温拉伸试验 每批任取2卷，每卷各取1个纵向试样 4.3.1 5.3.1 维氏硬度 每批任取2卷，每卷各取1个试样 4.3.2 5.3.2 工艺性能 杯突试验 每批任取2卷，每卷各取1个试样 4.4.1 5.4.1 弯曲试验 每批任取2卷，每卷各取1个横向试样 4.4.2 5.4.2 晶粒度 每批任取2卷，每卷各取1个试样 4.5 5.5 表面质量 逐卷 4.6 5.6 6.5 检验结果的判定 6.5.1 检验结果的数值按GB／T 8170的规定进行修约，并采用修约值比较法判定。 6.5.2 化学成分检验结果不合格时，判该批产品不合格。 6.5.3 室温拉伸试验、维氏硬度、杯突试验和弯曲试验检验中，如果有试样的检验结果不合格，则从该批产品(包括原检验不合格的那件产品)上取双倍数量的试样进行该不合格项的重复检验。若重复检验仍有试样不合格，判该批产品不合格。允许供方逐卷对不合格项进行检验，合格者交货。 6.5.4 外形尺寸及其允许偏差和表面质量检验结果不合格时，判该卷产品不合格。 7 标志、包装、运输、贮存和质量证明书 7.1 产品标志 在检验合格的产品上应做如下标志(或贴标签)： a) 供方名称或代号； b) 产品牌号、规格和状态； c) 产品批号； d) 本标准编号。 7.2 包装、运输、贮存和质量证明书 产品的包装、运输、贮存和质量证明书应符合GB／T 8888的规定。 8 订货单(或合同)内容 订购本标准所列产品的订货单(或合同)内应包括下列内容： a) 产品名称； b) 牌号、规格和状态； c) 尺寸精度； d) 弯曲试验(要求时)； e) 晶粒度(要求时)； f) 重量或件数； g) 本标准编号； h) 其他。