This document is developed in accordance with the rules given in GB/T 1.1-2020 Directives for standardization - Part 1: Rules for the structure and drafting of standardizing documents.
This document replaces GB/T 5313-2010 Steel plates with through-thickness characteristics. In addition to structural adjustments and editorial changes, the following main technical changes have been made with respect to GB/T 5313-2010:
a) The term "through-thickness properties" and its and definition have been added (see Clause 3 hereof);
b) The requirements for percentage reduction of area have been changed (see Notes 1 and 2 in Table 2 hereof; Table 2 of Edition 2010);
c) The specimen preparation of steel plate has been changed (see 6.2 hereof; 5.2 of Edition 2010);
d) The requirements for the steel plate specimen with extension have been changed (see 6.3 hereof; 5.3 of Edition 2010);
e) The requirements for the steel plate specimen without extension have been changed (see 6.4 hereof; 5.3 of Edition 2010);
f) The preparation and type diagrams of specimen have been changed (see Figure 1 in 6.3 and Figures 2 and 3 in 6.4 hereof; Figures B.1 to B.3 of Edition 2010);
g) The inspection rules have been changed (see 8.1 hereof; Clause 7 of Edition 2010);
h) The re-inspection rules have been changed (see 8.3.1 hereof; 7.3.1 of Edition 2010);
i) The supplementary requirements for steel plates, preparation and types of specimens have been deleted (see Annexes A and B to Edition 2010).
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. The issuing body of this document shall not be held responsible for identifying any or all such patent rights.
This document was proposed by China Iron and Steel Association.
This document is under the jurisdiction of SAC/TC 183 National Technical Committee on Iron and Steel of Standardization Administration of China.
This document was firstly issued in 1985, firstly revised in 2010, and this is the second revision.
Steel plate with through-thickness properties
1 Scope
This document specifies the designation expression methods, technical requirements, rough specimen and preparation of specimen, test methods and inspection rules of steel plates with through-thickness properties.
This document is applicable to the killed steel plates with a thickness of 15mm~400mm.
2 Normative references
The following documents contain provisions which, through reference in this text, constitute provisions of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
GB/T 228.1 Metallic materials - Tensile testing - Part 1: Method of test at room temperature
GB/T 2970 Method for ultrasonic testing of thicker steel plates
GB/T 17505 Steel and steel products - General technical delivery requirements
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1
through-thickness properties
deformation properties of a steel plate perpendicular to its surface, reflecting the ability of the steel plate to resist laminar tearing
Note: The through-thickness properties are usually evaluated by the percentage reduction of area obtained in the tensile test in the thickness direction.
4 Designation expression methods
The designation of steel plate with through-thickness properties consists of the original designation of the product and the grade (Z15, Z25 or Z35) of through-thickness properties.
Example: Q355GJDZ25
Q355GJD——the original designation of the product, which is high-performance building structure steel with minimum yield strength of 355MPa and quality grade of D;
Z25——the grade of through-thickness properties, with the minimum average of the percentage reduction of area of three specimens of 25%.
Foreword I 1 Scope 2 Normative references 3 Terms and definitions 4 Designation expression 5 Technical requirements 6 Preparation of rough specimens and test specimens 7 Test methods 8 Inspection rules
前言
本文件按照GB/T1.1—2020《标准化工作导则 第1部分：标准化文件的结构和起草规则》的规定起草。 本文件代替GB/T5313—2010《厚度方向性能钢板》。与GB/T5313—2010相比，除结构调整和编辑性改动外，主要技术变化如下： a) 增加了“厚度方向性能”的术语和定义(见第3章); b) 更改了对断面收缩率的要求(见表2的注1和注2，2010年版的表2); c) 更改了钢板的试样制备(见6.2，2010年版的5.2); d) 更改了钢板带延伸部分的试样的要求(见6.3，2010年版的5.3); e) 更改了钢板不带延伸部分的试样的要求(见6.4，2010年版的5.3); f) 更改了试样的制备和类型图(见6.3的图1、6.4的图2和图3，2010年版的图B.1～图B.3); g) 更改了检验规则(见8.1，2010年版的第7章); h) 更改了复验规则(见8.3.1，2010年版的7.3.1); i) 删除了钢板的补充要求、试样的制备和类型(见2010年版的附录A、附录B)。 请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。 本文件由中国钢铁工业协会提出。 本文件由全国钢标准化技术委员会(SAC/TC 183)归口。 本文件于1985年首次发布，2010年第一次修订，本次为第二次修订。